・ Evaluation method11SOLBIN CLL3 solutions have low viscosity and good fi lterability, enabling the design of ink with excellent nozzle suitability.NISSIN CHEMICAL INDUSTRY CO.,LTD.FUNCTIONAL MATERIALS FOR INKJET INK CATALOGUEComposition ratio(%)VAcVC8218Degree of polymerization260Molecular weight(Mn)K-value371.6×10⁴Glass transition point(℃)70■ 5 wt% SOLBIN was added to 10 wt% cyclohexanone (Anone).■The mixture was stirred at 50ºC for 60 minutes.■ The mixture stirred in step 2 was added to a mixed solution of 25 wt% propylene glycol monomethyl ether acetate (PMA) and 60 wt% ethylene glycol mono-n-butyl ether acetate (EBA), and this mixed solution was stirred for approximately 15 minutes.A 4 kg load was applied to 100 ml of the solution, and the time was measured until all of the solution passed through the fi lter.Measurement fi lter6.0◯Basic properties◯ Nozzle suitabilityFilterability・ Conditioning methodCLL302.04.08.012FilterFilter ・ Pore diameter : 1µmPore diameter : 1µm ・ Diameter : 25 mm ・ Diameter : 25 mmWeight:4kgSolution:100ml ・ SOLBIN : 5% ・ EBA : 60% ・ PMA : 25% ・ Cyclohexanone : 10%SOLBINEco-solvent-based pigment typeSOLBIN CLL3SOLBIN CLL3 is a vinyl chloride-vinyl acetate copolymer resin that is soluble in eco solvent thanks to the technology of copolymerization with vinyl acetate. It also exhibits the excellent pigment dispersibility characteristic of vinyl chloride resins.
元のページ ../index.html#12